FLAME RETARDANT HEAVY WALL HEAT SHRINKABLE TUBING WITH HOT MELTING ADHESIVE BH-FRA3
- Applications: Flame retardant heavy wall heat shrinkable tubing with hot melting adhesive suitable for protecting electrical splices,cable terminations and joints where flame retardant and electrical insulation and water proof are required
- Characteristics: BH-FRA3 is made from radiation cross-linked polyolefin with hot melt Adhesive
-
Operating temperature range: Shrink temperature: 120℃
Operating temperature: -55℃ to 110℃ - Approvals / Specifications: RoHS
- Colors: Black, Red, Gray
| Normal size(mm) | As supplied(mm) | After recovered (mm) | *Style | Standard length(mm) | |
| Inside diameter(min.) | Inside diameter(Max.) | Wall thickness(Nom.) | |||
| 9/3 | 9 | 3 | 2 | O | 1000-1500 |
| 13/4 | 13 | 4 | 2.5 | O | 1000-1500 |
| 22/6 | 22 | 6 | 2.7 | O | 1000-1500 |
| 33/8 | 33 | 8 | 3.2 | O | 1000-1500 |
| 40/12 | 40 | 12 | 4.1 | O | 1000-1500 |
| 55/16 | 55 | 16 | 4.1 | O | 1000-1500 |
| 75/22 | 75 | 22 | 4.1 | O | 1000-1500 |
| 95/29 | 95 | 29 | 4.1 | O | 1000-1500 |
| 115/34 | 115 | 34 | 4.3 | O | 1000-1500 |
| 130/36 | 130 | 36 | 4.3 | O | 1000-1500 |
*style “O”: round or oval
|
Property |
Test Method |
Typical Data |
|
Tensile strength |
ASTM D 2671 |
≥14MPa |
|
Tensile strength after aging |
ASTM D 2671/158℃, 168hrs. |
≥12MPa |
|
Longitudinal change after shrinking |
ASTM D 2671 |
0, -10% |
|
Elongation at break |
ASTM D 2671 |
≥300% |
|
Elongation at break after aging |
ASTM D 2671/120℃,168hrs. |
≥200% |
|
Dielectric strength |
IEC 243 |
≥20KV/mm |
|
Heat shock (4hrs. at 225℃) |
ASTM D 2671 |
No cracking or flowing |
|
Volume resistance |
IEC 93 |
≥1014Ω.cm |
|
Flammability |
SAE-AMS-DTL-23053/5 |
Self extinguish in 30 sec. |
|
Thermoplastic Adhesive |
||
|
Water absorption |
ISO 62 |
<0.2% |
|
Softening point |
ASTM D E28 |
85℃ |
|
Peel strength (PE) |
DIN 30672 |
4 N/cm |
|
Copper stability |
ASTM D 2671 |
Non-corrosive |
|
Resistance to fungus and decay |
ISO 846 |
Pass |