Normal size(mm)
|
As supplied(mm)
|
After recovered (mm)
|
*Style
|
Standard length(mm)
|
|
Inside diameter(min.)
|
Inside diameter(Max.)
|
Wall thickness(Min)
|
|
22/6
|
22
|
6
|
2.5
|
O
|
1000-1500
|
|
33/8
|
33
|
8
|
2.5
|
O
|
1000-1500
|
|
40/12
|
40
|
12
|
2.5
|
O
|
1000-1500
|
|
55/16
|
55
|
16
|
2.7
|
O
|
1000-1500
|
|
65/19
|
65
|
19
|
2.8
|
O
|
1000-1500
|
|
75/22
|
75
|
22
|
3.0
|
O
|
1000-1500
|
|
95/25
|
95
|
25
|
3.0
|
O
|
1000-1500
|
|
115/34
|
115
|
34
|
3.0
|
O
|
1000-1500
|
|
140/42
|
140
|
42
|
3.0
|
O
|
1000-1500
|
|
160/50
|
160
|
50
|
3.0
|
O
|
1000-1500
|
|
180/58
|
180
|
58
|
3.0
|
O
|
1000-1500
|
|
200/65
|
200
|
65
|
3.0
|
O
|
1000-1500
|
|
235/65
|
235
|
65
|
3.0
|
O
|
1000-1500
|
|
265/75
|
265
|
75
|
3.0
|
O
|
1000-1500
|
|
300/85
|
300
|
85
|
3.0
|
O
|
1000-1500
|
*Style : “ O” round shape or Oval
|
Property
|
Test Method
|
Typical Data
|
|
Tensile strength
|
ASTM D 2671
|
≥14MPa
|
|
Tensile strength after aging
|
ASTM D 2671/158℃, 168hrs.
|
≥12MPa
|
|
Longitudinal change after shrinking
|
ASTM D 2671
|
0, -10%
|
|
Elongation at break
|
ASTM D 2671
|
≥300%
|
|
Elongation at break after aging
|
ASTM D 2671/120℃,168hrs.
|
≥200%
|
|
Dielectric strength
|
IEC 243
|
≥20KV/mm
|
|
Heat shock (4hrs. at 225℃)
|
ASTM D 2671
|
No cracking or flowing
|
|
Volume resistance
|
IEC 93
|
≥1014Ω.cm
|
|
Flammability
|
SAE-AMS-DTL-23053/5
|
Self extinguish in 30 sec.
|
|
Thermoplastic adhesive
|
|
Water absorption
|
ISO 62
|
<0.2%
|
|
Softening point
|
ASTM D E28
|
85℃
|
|
Peel strength (PE)
|
DIN 30672
|
4 N/cm
|
|
Copper stability
|
ASTM D 2671
|
Non-corrosive
|
|
Resistance to fungus and decay
|
ISO 846
|
Pass
|