Normal size
|
As supplied (mm)
|
After recovered (mm)
|
Standard length
(m/spool)
|
|
(mm)
|
(inch)
|
Inside diameter(Min.)
|
Wall thickness(mm)
|
Inside diameter(Max.)
|
Wall thickness(Min.)
|
|
1.5/0.5
|
1/16
|
1.6
|
0.15
|
0.5
|
0.45
|
200
|
|
3.0/1.0
|
1/8
|
3.2
|
0.18
|
1.0
|
0.55
|
200
|
|
4.5/1.5
|
3/16
|
4.8
|
0.20
|
1.5
|
0.60
|
100
|
|
6.0/2.0
|
1/4
|
6.4
|
0.22
|
2.0
|
0.65
|
100
|
|
9.0/3.0
|
3/8
|
9.5
|
0.25
|
3.0
|
0.75
|
100
|
|
12.0/4.0
|
1/2
|
12.7
|
0.25
|
4.0
|
0.80
|
50
|
|
18.0/6.0
|
3/4
|
19.1
|
0.35
|
6.0
|
0.90
|
50
|
|
24.0/8.0
|
1
|
25.4
|
0.45
|
8.0
|
1.20
|
50
|
|
39.0/13.0
|
1 1/ 2
|
39.0
|
0.50
|
13.0
|
1.25
|
50
|
Special size, cut pieces are available on request.
|
Property
|
Test Method
|
Typical Data
|
|
Tensile strength
|
ASTM D 2671
|
16MPa
|
|
Elongation at break
|
ASTM D 2671
|
800%
|
|
Tensile strength after aging at175℃for 168 hrs
|
ASTM D 2671
|
14MPa
|
|
Elongation after aging at175℃for 168 hrs.
|
ASTM D 2671
|
350%
|
|
Flammability
|
UL 224 / VW-1
SAE-AMS-DTL-23053/5
|
Pass
|
|
Heat shock (250℃/ 4 hrs.)
|
ASTM D 2671
|
No cracking
|
|
Cold bend test (-55℃/ 4 hrs.)
|
ASTM D 2671
|
No cracking
|
|
Dielectric strength
|
ASTM D 150
|
20KV/mm
|
|
Volume resistance
|
ASTM D 876
|
1014Ω .cm
|
|
Copper Corrosion
|
UL 224
|
Pass
|
|
Water absorption
|
ASTM D 570
|
0.15%
|
|
Chemical resistance
|
SAE-AMS-DTL-23053/5
|
Pass
|
|
Longitudinal shrinkage
|
UL 224
|
0±5%
|
|
Eccentricity
|
UL 224
|
30%
|